Photocatalytic activity of coatings based on titanium oxides deposited by reactive magnetron sputtering method
Article Sidebar
Main Article Content
Abstract
The aim of this project is to measure the photocatalytic activity of titanium oxides thin layers deposited by reactive magnetron sputtering method. The coatings were deposited onto silicon substrates in gas misxture of Ar and O2 and as target was used pure titanium. Chemical composition of coatings was varied by change of O2 flow. As results, it was obtained a chemical composition Ti1-xOx where x is from 0,25 to 0,45. According to the adhesion scratch test, the lowest critical load was 14,43 N and highest was 72,01 N. Results from photocatalytic activity indicates that the samples were not active due to the acid orange in which they were submerge presented no change of color after the UV light exposition.
Article Details
Los autores conservan los derechos de autor y ceden a la revista el derecho de la primera publicación y pueda editarlo, reproducirlo, distribuirlo, exhibirlo y comunicarlo en el país y en el extranjero mediante medios impresos y electrónicos. Asimismo, asumen el compromiso sobre cualquier litigio o reclamación relacionada con derechos de propiedad intelectual, exonerando de responsabilidad a la Editorial Tecnológica de Costa Rica. Además, se establece que los autores pueden realizar otros acuerdos contractuales independientes y adicionales para la distribución no exclusiva de la versión del artículo publicado en esta revista (p. ej., incluirlo en un repositorio institucional o publicarlo en un libro) siempre que indiquen claramente que el trabajo se publicó por primera vez en esta revista.