Synthesis of CeO2: sol-gel properties and characterization of the obtained nanoparticles
Article Sidebar
Main Article Content
Abstract
We propose an efficient sol-gel synthesis of a nanoparticled cerium oxide (IV) method. AFM micrographs confirm the presence of nanoparticles. Furthermore, TGA, FTIR and XRD measurements validate the absence of impurities. Scherrer’s law reveals a particle size of 11 nm, whereas DLS analysis shows an average diameter of 9.55 nm. Notably, viscosity and concentration behave proportionally. Contact angle measurements show that is more feasible to coat silicon (110) substrate than pure aluminum. Moreover, a filter for ultraviolet radiation is obtained when particle concentrations are larger than 13.74 mg/cm3.
Article Details
Los autores conservan los derechos de autor y ceden a la revista el derecho de la primera publicación y pueda editarlo, reproducirlo, distribuirlo, exhibirlo y comunicarlo en el país y en el extranjero mediante medios impresos y electrónicos. Asimismo, asumen el compromiso sobre cualquier litigio o reclamación relacionada con derechos de propiedad intelectual, exonerando de responsabilidad a la Editorial Tecnológica de Costa Rica. Además, se establece que los autores pueden realizar otros acuerdos contractuales independientes y adicionales para la distribución no exclusiva de la versión del artículo publicado en esta revista (p. ej., incluirlo en un repositorio institucional o publicarlo en un libro) siempre que indiquen claramente que el trabajo se publicó por primera vez en esta revista.